摘要：环氧云铁中层漆用于中间涂漆究竟起到一个怎样的作用有很多人都不是很清楚，而且对你环氧云铁中层漆和环氧云铁防锈漆来说有怎样的不同之处存在很大的疑惑，下面我们就根据这样的问题作出一个解释。

　　Abstract: the epoxy micaceous iron oxide middle paint used for intermediate paint what plays a role with a lot of people are not very clear, but also for your paint and epoxy micaceous iron oxide antirust paint epoxy micaceous iron oxide middle, what is the difference of existence a lot of doubt, we can according to the next question to make an explanation.

　　环氧云铁中层漆的作用

　　1、 加强防锈防腐的效果：环氧云铁中层漆产品的屏蔽性能极好，在增加涂层物理防锈效果的基础上，苛刻环境下多种物质都不宜渗透到地材之处，所以它的涂层十分强大。

　　1, enhance the effect of the rust corrosion: epoxy micaceous iron middle product shielding performance is very good, on the basis of increased physical antirust coating effect, harsh environment many kinds of material are not infiltrate into ground material, the coating so it is quite powerful.

　　2、 降低涂装成本：有些施工时需要对油漆的涂层厚度有一个明显的影响。钢结构防腐涂层设计总厚度规范一般要达到120um,或者150um，采用中间漆也是为了达到防腐效果，同样的厚度成本会降低的多。

　　, to reduce the coating cost: when some construction need to paint coating thickness has a significant impact. Steel structure anticorrosion coating design of total thickness specification to achieve 120 um, general or 150 um, adopt intermediate paint is also in order to achieve anticorrosive effect, can reduce the thickness of the same cost.

　　3、 延长防腐期限：同样厚度的涂层，在符合设计规范标准的情况下，采用中间漆的防腐层能给又更强的期限。

　　3, extend preservation period, the same thickness of coating, in the case of comply with the design standard, adopt the intermediate paint coating can give more time again.

　　特殊用途：环氧云铁中层漆用于表面的封闭漆，在面漆和配套环氧云铁中层漆的气体下就能给又更高效的应用反应。

　　Special purpose: epoxy micaceous iron oxide on the surface of the middle paint for sealing paint, the paint and epoxy micaceous iron middle gas under reaction and can give more efficient application.

　　环氧云铁中层漆与环氧云铁防锈漆的区别

　　1、 在环氧树脂中加入了云铁制成的防锈产品，是醇酸、酚醛云铁之后，广泛的应用于防腐涂料体系中，作为防锈底油漆以及中间油漆使用。

　　1, joined the cloud in the epoxy resin iron rust products, is the alkyd and phenolic micaceous iron oxide, widely used in the anticorrosion coating system, as an antirust paint bottom and intermediate paint is used.

　　2、 环氧云铁防锈油漆最早是作为防锈底漆来使用的，而云铁的涂膜中有着非常好的渗透作用。广泛的用于重防腐体系汇总作为中间漆使用应该十分注意配套性。

　　2, epoxy micaceous iron oxide antirust paint was first used as antirust primer, and micaceous iron oxide coating has a very good osmosis. Widely used for heavy-duty system summary used as intermediate paint should be very outstanding.

　　3、 在此基础上，开发出来的环氧云铁中层漆中加入了更多的填料肠粉，也就进一步的加强了屏蔽效果，单纯的作为中间漆使用但是不能作为防锈。

　　3, on this basis, the development of epoxy micaceous iron middle packing im powder, adding more will further strengthen the shielding effect, simple used as intermediate paint but no rust.

　　4、原浆型的环氧云铁中间漆固体成分达不到80％以上，云铁成分占到颜料的比例能给对厚膜型施工厚度有一定的限制。环氧云铁中层漆最好与富锌 配合使用，增加整4, protoplasmic type epoxy micaceous iron oxide intermediate paint solids to reach more than 80%, cloud with iron accounted for the proportion of pigment can give the thickness of thick film type construction has certain restrictions. Epoxy micaceous iron oxide intermediate coating is best used with zinc, increases the rust resistance of coating system.个涂层的体系防锈性能。